Finishes

Powder coating is only suitable for metal parts since it relies on an electrostatic charge existing between the powder and the part so that the powder sticks. It is thus a factory based process.

Parts are first degreased, hung on a conductive hook, sprayed with powder then passed though an over at about 200 degC for 10 mins. The powder melts, flows and cures resulting in a corrosion resistant, hard finish. Colours are normally RAL or BS standard colours in matt, semi-gloss or gloss finishes with optional thickening effects such as leatherette.

Powder coating is generally applied to zintec, aluminium (after alochroming) and stainless steel.

Wet Spray painting is more flexible than powder coating since paint can be applied to both metallic and non-metallic parts. It is more expensive than Powder Coating, far more dependant on the skill of the operator and curing temperatures are higher and longer than for Powder Coating.

With regards to sheet metalwork, wet spray tends be used where thin, hard wearing or very high quality gloss finishes are required or where there is a legacy issue such as with old military specifications.

As with Powder Coating, a wide range of RAL and BS standard colours are available in various finishes.

Painting is in small quantities in colours which are not popular can result is high minimum charges.

ElectroPlating is the process of depositing a metal onto a conductive surface, normally another metal. For example zinc on steel for corrosion resistance, chromium on steel for a shiny surface, tin on steel for hygiene, copper on zinc (coins) or gold on plastic for electrical conductivity using Electroless plating.

In Electoplating, the anode (positive) is made of the metal to be deposited (for example zinc) and the cathode (negative) is the part to be plated (for example steel). Both are immersed in a bath of conductive fluid called an electrolyte, current is then applied and plating takes place. The higher the current and the longer it is applied, the thicker the plating and the size of the part will be altered.

Electroless plating uses only one electrode and no external source of electric current or baths are used. Metal can be deposited on non-metallic surfaces as in PCB’s. The is a low cost process, the plating is of uniform thickness but it is slow and thick plating is hard to achieve.

A passivation process can be applied to Plating to further increase corrosion resistance and passivation can be clear, yellow or black.

In GW, the most common forms of plating are zinc plating mild steel for corrosion resistance and chromium plating to achieve a shiny surface.

Anodising is a process applied to aluminium to stop white blisters of corrosion forming which causes blackening on touch.

The aluminium is pre-treated in an alkaline bath based on sodium hydroxide then rinsed clean. The anodization process takes place in an electrolytic bath based on sulphuric acid using the aluminium as the anode. This changes the surface of the aluminium to prevent further corrosion but does not seal it.

Because the surface is porous, the aluminium can optionally be coloured in a bath of organic dye typically blue, black, red, orange, green, purple or bronze to achieve attractive finishes.

An optional forth stage to Anodising is to seal the oxide layer by immersion in a bath containing a chemical sealant.

Iriditing of aluminium  is done by applying a thin film of chromate to create a corrosion-resistant golden coloured coating which also serves as an excellent primer for powder coating.

Iridited parts retain their electrical conductivity, the process adds no weight nor is the component altered in size.

The Iridite film repairs itself if scratched, marks such as fingerprints wipe clean and parts are pleasant to handle. Iridite also repels water providing excellent protection against moisture.

Iridited aluminium parts are commonly used internally and externally in electrical and electronic products.